| Title |
Analysis of Wall Blackening Reason in Ceramic Metal Halide Lamp by Shape of Arc-tube and Degradation Condition |
| Authors |
김우영(Kim, Woo-Young) ; 이세일(Lee, Se-Il) ; 양종경(Yang, Jong-Kyung) ; 정영기(Jeong, Young-Gi) ; 박대희(Park, Dae-Hee) |
| Keywords |
Ceramic metal halide lamp ; Wall blackening ; Arc-tube ; Degradation ; PCA tube ; HID |
| Abstract |
In order to analyze the reason of wall blackening, which affect the decline of lifetime in a ceramic metal halide lamp, we carried out the deterioration of ceramic tubes by a change in operating conditions with arc tubes of two types of spherical and cylindrical, and we have confirmed the cause of wall blackening through the analysis of element composition and spectrum from SEM/EDS and spectrum analyzer. Wall blackening of tungsten was shown by sputtering from ignition in 20 minute on/off condition and wall blackening from chemical reaction between PCA wall and rare earth halides was shown significantly in a condition without on/off test. Especially, the wall blackening and the decline of luminous flux were reduced by inner convection in spherical type arc tube. Moreover, the color temperature and color coordinate were changed by reduction of emission spectrum of Dy which causes the chemical reaction with PCA wall. |